Steel wire and iron wire have a lot of similarities, but carefully distinguish, you will find that they are not only different in the material, but also in the product characteristics are very different. So when choosing, make sure you make a clear distinction between the two. Steel wire factory introduces steel wire carbon structure steel made above, generally not galvanized, used for machinery, spring. Black and hard; Iron wire: low carbon steel (mild steel), galvanized, used for joining and wrapping. It’s white and soft.
The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.
Life said “wire”, in fact, is “low carbon steel wire”, carbon content in 0.2% below. The surface is usually coated with zinc coating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. Life said “steel wire”, is the carbon content of about 0.6% of the “carbon steel wire”, or carbon content of about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. The use of words such as winding ordinary spring and so on.
Annealed wire is a kind of soft iron wire made of low carbon steel by cold drawing, heating, constant temperature and heat preservation. The composition of the wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet is rolled into 6.5mm thick steel bar, that is, the wire rod, and then it is put into the wire drawing device to draw the wire of different diameter, and gradually reduce the aperture of the drawing disk, cooling, annealing, plating and other processing technology to make a variety of different specifications of the wire.
Annealed wire is mainly through low carbon steel heating, hot drawing, constant temperature and other processes made into soft iron wire, because in the use of different, so there are different in the production process, made of a variety of specifications. Annealed wire can be widely used, mainly because annealed wire and other kinds of iron wire, has many advantages.
Regular maintenance and maintenance, save a lot of time, but also save the cost of maintenance and maintenance. With good stability, corrosion resistance, greatly prolong the service life. There are many kinds, which can be selected according to different uses. The device for making annealed wire is simple, and the utilization rate of the device is improved.