The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.
A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.
B. When the thickness of the plating is greater than 4 mm, the zinc adhesion should not be less than 610g/m, that is, the average thickness of the zinc layer should not be less than 86 microns.
C, coating uniformity: galvanized layer is basically uniform with copper sulfate solution test etched five times without exposing iron.
D, coating adhesion; The zinc layer of the plating parts should be firmly combined with the base metal with sufficient adhesion strength, and will not fall off or bulge after the hammer test.