Hot dip galvanizing of steel plate is also called hot dip galvanizing. Zinc ingots are melted in the tropics and some auxiliary materials are added in hot dip galvanizing. The steel grid parts are then soaked in a galvanizing tank and a galvanizing layer is attached to the steel plate. The strength of hot dip galvanizing depends on its corrosion resistance, and the adhesion and hardness of galvanized sheet are better. The amount of galvanized steel plate after galvanizing. So this is the general amount of zinc.
The composition of hot dip galvanizing layer is composed of hot dip galvanizing layer, which is composed of iron zinc alloy between iron matrix and surface pure zinc layer. The shape of the workpiece is formed by the iron zinc alloy layer in hot dip, so that the iron and pure zinc layer touch outstanding. When the iron workpiece is immersed in a molten zinc solution, the initial zinc and iron (body) are formed at the interface. This is a crystal made up of zinc atoms in the solid metal iron. When two metal atoms are fused together, the gravitational force between the atoms is very small.
Thus, when zinc is sufficient in a solid melt, the two atoms of zinc and iron disperse with each other. The zinc atoms in the iron matrix are moved into the lattice of the matrix, and the iron elements are gradually formed into alloys. The zinc composition of iron and intermetallic compound FeZn13 in molten zinc solution and the bottom of hot galvanized sheet can be used as zinc slag. The pure zinc layer composed of zinc leaching solution is hexagonal crystal.
When the temperature is running at the same temperature and the same heat is stored, the amount of iron dissolved is not the same. At around 500, the loss of iron increases sharply with the addition of temperature and insulation. It is lower or higher than 480~ 510c, and the loss of epitaxial iron is slower, and it is difficult to catch up with the duration. Therefore, everyone will call 480~ 510c the malignant melting zone.
In this temperature range, the zinc solution is severely corroded to the workpiece and the zinc pot, and the iron is lost at 560 degrees Celsius to add obviously, and the zinc will be the iron substrate above 660 degrees Celsius, zinc slag will be added quickly, plating cannot be used. Therefore, electroplating is carried out in the range of 430~450 degrees Celsius.