Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.
Cooling can be in the groove close row of thin wall plastic pipe, through the flow of tap water for cooling, can also be used as a temperature control device titanium pipe. In the process of electroplating galvanized wire, it is necessary to stir the plating solution to obtain the composite coating with particles dispersing in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.
The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion to the matrix. Galvanized wire can be zincate galvanized or chloride galvanized process, should use appropriate additives to obtain the low carbon steel wire standard requirements of the coating. When galvanized wire after light plating should be light treatment. Control the temperature of the bath of galvanized wire.
Great attention should be paid to pickling of large rolls of galvanized wire. Acid is highly corrosive. Therefore, when adding acid, the acid must be poured into the water, and it is along the wall of the cylinder, and not thrown down at once, so as not to cause splashing. Remember the order of acid pouring, acid into water rather than water into acid, water into acid will cause splashing and boiling, when pouring acid must wear protective glasses, beside must ensure that there are no non-professional people watching, so as not to cause some acid splashing danger.
Post time: 27-10-22