Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
Because of the pre-tension given to the packaging and binding of galvanized wire, it has the excellent characteristics of low relaxation value, small stress loss, good stability after loading, not easy to deformation, no fracture, strong elasticity, ordinary steel lines and rebar are difficult to compare. The use of advanced galvanized finishing process, therefore, the use of hot-dip galvanized steel wire construction, not only good corrosion resistance, but also beautiful and generous. The product has the characteristics of smooth surface, high dimensional accuracy, good uniformity of zinc layer and strong adhesion.
Post time: 25-04-23