Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.
In the electroplating tank through the current unidirectional make zinc plating on the metal surface gradually, the production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 micron, the appearance is bright, smooth, beautiful, poor corrosion resistance, generally will rust in a few months. The production process of hot wire plating mainly includes: preparation of the original plate → pre-plating treatment → hot dip plating → post-plating treatment → finished product inspection, etc. According to custom often according to plating pretreatment method.
Different hot dip galvanizing process is divided into two categories of annealing outside the line and annealing in the line, hot dip galvanizing is in the hot melt zinc liquid immersion plating, production speed, thick but uneven coating, the market allows Z low thickness of 45 microns, Z high can reach more than 300 microns. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.
Hot dip galvanizing, also known as hot dip zinc, is the method of forming a layer of zinc coating on the surface of the workpiece after oil removal and rust removal, showing a clean and infiltrating surface, immediately immersed in the plating tank of zinc melting in advance. Cold galvanizing is the same after the removal of oil, in addition to lure, showing no pollution, infiltration of the workpiece hung into a special electroplating tank on the cathode, the anode with zinc. Switch on the DC power supply, zinc ions on the anode migrate to the cathode, and discharge on the cathode, so that the workpiece is coated with a layer of zinc layer hot dip galvanizing method.
Hot wire coating is thick, generally 30-60 microns, coating corrosion resistance is high. Suitable for outdoor work of steel parts, such as highway fence, power tower, large size fasteners and other relatively “rough” workpiece long-term rust prevention. The hot dip galvanized wire is made of high quality carbon structural steel by drawing and hot dip galvanizing. Widely used in the manufacture of wire mesh, highway protection and construction engineering. It has the characteristics of thick coating, strong corrosion resistance and firm coating. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire.