In order to remove defects such as surface film layer and surface inclusion of large roll galvanized wire, it can be treated by conventional technology. The presence of small homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of too many solid particles can cause explosion. Activated carbon mat to remove surface active substances, or through filtration to make the foam less stable, these are effective measures; Other measures should also be taken to minimize the intake of surface active substances. The electroplating speed can be significantly reduced by the introduction of organic matter.
Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank. Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air. In humid air or small water containing carbon dioxide and oxygen, the surface of large rolls of galvanized wire will generate a layer of basic zinc carbonate based thin film layer, which can delay the corrosion rate of zinc layer.
Galvanized wire in acid, alkali, sodium chloride aqueous solution of poor corrosion resistance, in the atmosphere containing carbon dioxide and hydrogen sulfide, as well as Marine atmosphere is not corrosion resistance. In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded. Galvanized wire and general wire is very different, general wire is cheap, and because the iron is not very stable, easy to rust in the wet place, so the stability is not very good, the life is not very long.
Galvanized wire is coated with a layer of stable zinc on the outside of the wire, and the zinc layer is used to protect the wire and make the service life of the wire longer. In the production of galvanized wire, the wire should be pickled. Pickling is to use some acid mist or acid liquid to wash away some oxides on the surface of iron, that is, rust, and some other corrosion, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanized.
When pickling, we should pay great attention to the acid has a strong corrosion, so when adding acid, we must pour acid into water, and it is along the wall of the cylinder, not a splash down, so as not to cause splash. Remember the order of pouring acid, acid into water rather than water into acid, water into acid will cause splashing and boiling, when pouring acid must wear protective glasses, must ensure that there are no non-professional onlookers, so as not to cause some risk of splashing acid.