The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.
During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
But there are some necessary precautions in the production of galvanized wire. Remove all tools and piles on the work site and equipment that hinder activities, and slowly put the wire into the cylinder during pickling to prevent acid splashing on the body. When adding acid, the acid must be slowly poured into the water. Do not pour water into the acid to prevent acid spillage and injury. Workers should wear protective glasses when working. Then in the handling of wire and other items, it is strictly prohibited to push hard.
Pay attention to safety in line collection and operation, others without the consent of the monitor, Ben have to get on the bus operation. The reels should be placed lightly, stacked firmly and neatly, not more than 5 reels. Direct contact with acid and alkali must be prohibited. When the acid fog exceeds the specified target of the state, measures should be taken to control it in time, otherwise production is not allowed.
Pure zinc is more stable in dry air. In moist air or water containing carbon dioxide and oxygen, the surface will generate a layer of basic zinc carbonate based thin film layer, which can delay the corrosion rate of zinc layer. Comparison of corrosion resistance of zinc coating in aqueous solution of acid, alkali and sodium chloride; It is also resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in oceanic atmospheres; In high temperature and high humidity air and contain organic acid atmosphere is small, galvanized layer is also easy to be corroded.